Mining · Quarry · Earthmoving
Bimetallic wear parts that outlast the rock.
700 HB white-iron wear faces bonded to weldable steel. Chocky bars, wear buttons and wear plates for buckets, chutes and hoppers.
Featured line — in stock now
Chocky Bars
White-iron wear face (700+ HB) metallurgically bonded to a mild-steel backing strip. The soft backing welds with standard consumables while the hard face resists gouging and sliding abrasion.
CB-6010
60×10×25 mm
CB-9020
90×20×25 mm
CB-12025
120×25×30 mm
CB-15025
150×25×40 mm
- Wear face
- High-chrome white iron, 27% Cr
- Hardness
- 700 – 750 HB (63 HRC)
- Backing
- Mild steel, weldable
- Bond
- Vacuum-brazed metallurgical bond
- Welding
- E7018 / ER70S-6, no preheat required
- Service temp.
- Up to 350 °C
Also available
Wear Buttons
Round domed buttons to protect high-impact wear points.
Also available
Wear Plates
Large-format bimetallic plate for chutes, liners and hoppers.
700+
HB wear face
27%
Chromium content
3–5×
Life vs. Q&T plate
No
Preheat to weld
Where it goes
All applications →Buckets
Chocky bars across the bucket bottom and sides, buttons on heel and corner wear points. Extends shell life on loaders, excavators and draglines.
Chutes
Wear plates on sliding surfaces and chocky bars in a grid to trap material and form a self-renewing dead-bed.
Hoppers
Plate liners in impact zones, buttons on feed lips and transitions where lumps strike hardest.
From quote to bucket in three steps
01
Build your quote
Pick products, sizes and quantities in the online quote builder — custom sizes welcome.
02
We confirm pricing
Our team confirms pricing, lead time and freight within one business day.
03
Weld & go
Parts arrive ready to weld with standard consumables — no preheat, no special procedure.